PUR Hot Melt Adhesive
PUR hot melt adhesive for furniture edge banding, panel lamination, woodworking, bookbinding and industrial bonding. Share your substrate, machine type and target performance to request sample matching and quotation for Vietnam, Indonesia and other export projects. For faster quoting, send your purchase volume and application details.
PUR Technical Data & Applications
Furniture Woodworking Edge Banding PUR Hot Melt Adhesive
Appearance: Solid
Colors: Rice white, light yellow, pure white, transparent, white semi-transparent
| Model | Operate Temperature | Viscosity | Ambient Temperature | Product Advantages |
|---|---|---|---|---|
| 508.7 | 130-160 deg C | 60000-90000 mPa.s (150 deg C) | 0-38 deg C | Good initial adhesion and cost-effectiveness |
| 508.7W | 130-160 deg C | 60000-90000 mPa.s (150 deg C) | 0-38 deg C | Good initial adhesion and cost-effectiveness |
| 608.7S | 130-160 deg C | 70000-100000 mPa.s (150 deg C) | -5-43 deg C | Wide applicability and high initial adhesion strength |
| 608.7W | 130-160 deg C | 70000-100000 mPa.s (150 deg C) | -5-43 deg C | Wide applicability and high initial adhesion strength |
| 708.7S | 130-160 deg C | 55000-90000 mPa.s (150 deg C) | -5-40 deg C | Widely applicable regardless of winter or summer |
| 708.7W | 130-160 deg C | 55000-90000 mPa.s (150 deg C) | -5-40 deg C | Widely applicable regardless of winter or summer |
| 808.6S | 130-160 deg C | 40000-60000 mPa.s (150 deg C) | 0-40 deg C | High transparency and initial adhesion strength |
| 808.6W | 130-160 deg C | 40000-60000 mPa.s (150 deg C) | 0-40 deg C | High transparency and initial adhesion strength |
Application Scenarios
- 508.7, 508.7W, 608.7S: suitable for customized furniture and solid wood doors.
- 608.7W, 708.7S, 708.7W: suitable for customized furniture, high-end cabinet doors and solid wood doors.
- 808.6S, 808.6W: suitable for edge sealing of aluminum honeycomb substrates.
Wood Door Wrapping Profile PUR Hot Melt Adhesive
Appearance: Solid
Color: Light yellow transparent
| Model | Operate Temperature | Viscosity | Adapt to Material | Product Advantages |
|---|---|---|---|---|
| 610.6 | 130-160 deg C | 50000-70000 mPa.s (150 deg C) | Melamine paper, veneer, CPL and other thick / hard film materials | High initial adhesion, strong peel strength |
| 610.8 | 130-160 deg C | 15000-30000 mPa.s (150 deg C) | Melamine paper and thinner CPL film materials | Good low-temperature adaptability, high initial adhesion and high peel strength |
Bookbinding PUR Hot Melt Adhesive
| Model | Operate Temperature | Viscosity | Adapt to Machine | Product Advantages |
|---|---|---|---|---|
| 710.1 | 130-160 deg C | 10000-15000 mPa.s (130 deg C) | Single head linear machine / elliptical machine | Excellent adhesion strength after curing, with moisture resistance, cold resistance, water resistance and chemical resistance |
Application Scenarios
- 710.1: suitable for magazines, commercial printing, catalogs, paperbacks, dictionaries and thicker books.
Textile PUR Hot Melt Adhesive
| Model | Operate Temperature | Viscosity | Packaging | Product Advantages |
|---|---|---|---|---|
| 720.1 | 100-120 deg C | 3500-5500 mPa.s (120 deg C) | 5 gallon / 55 gallon iron drum | Good initial adhesion, positioning effect and high peel strength |
| 720.2 | 100-120 deg C | 4500-6500 mPa.s (120 deg C) | 5 gallon / 55 gallon iron drum | Wide application range, environmentally friendly, odorless and solvent resistant |
| 760.1 | 120-130 deg C | 9500-10500 mPa.s (120 deg C) | 310 ml aluminum tube | Excellent feel, high bonding strength, soft handfeel and efficient water resistance |
| 760.2 | 120-130 deg C | 11000-13000 mPa.s (120 deg C) | 310 ml aluminum tube | Odorless, suitable for a wide range of fabrics, with good initial adhesion and high bonding strength when heated again |
Application Scenarios
- 720.1: mainly used for bonding fabrics, sponge, EVA and SBR materials.
- 720.2: suitable for underwear, home textiles, leisure textiles and automotive interior fabrics.
- 760.1, 760.2: suitable for underwear, home textiles and interior fabrics.